Perbandingan komposisi kimia
| Al2O3 | SiO2 | Fe2O3 | TiO2 | |
| Pasir Keramik Lebur (ireng) | 72,73% | 19,67% | 2,28% | 1,34% |
| Cerabeads | 60,53% | 31,82% | 2,07% | 2,74% |
| Pasir Keramik Sintered Kaist | 57,27% | 32,74% | 2,73% | 2,82% |
| Pasir Keramik liyane | 52,78% | 38,23% | 2,49% | 1,68% |
| pasir kalsinasi (pasir silika) | 3,44% | 90,15% | 0,22% | 0,14% |
Perbandingan sifat fisik lan kimia
| Kapadhetan akeh (g/cm3) | Refractoriness (℃) | Koefisien ekspansi termal (20-1000 ℃) （10/℃） | Koefisien sudut | Ignition loss (%) | |
| Pasir Keramik Lebur (ireng) | 1.83 | ＞ 1800 | <6 | <1.06 | <0.1 |
| Cerabeads | 1.72 | 1825 | 4.5-6.5 | <1.15 | <0.1 |
| Pasir Keramik Sintered Kaist | 1.58 | ＞ 1800 | 4.5-6.5 | <1.1 | <0.1 |
| Pasir Keramik liyane | 1.53 | ＞ 1750 | 4.5-6.5 | <1.15 | <0.1 |
| pasir kalsinasi (pasir silika) | 1.59 | 1450 | 20 | <1.30 | <0.1 |
Perbandingan indeks pasir dilapisi saka macem-macem pasir
| Kekuatan tarik panas (MPa) | Kekuatan tarik (MPa) | Suhu dhuwur lan wektu tekanan (1000 ℃) (S) | Breathability （Pa） | Kapadhetan akeh (g/cm3) | Laju ekspansi linier (%) | |
| Pasir Keramik Lebur (ireng) | 2.1 | 7.3 | 55 | 140 | 1.79 | 0.08 |
| Cerabeads | 1.8 | 6.2 | 105 | 140 | 1.68 | 0.10 |
| Pasir Keramik Sintered Kaist | 2.0 | 6.6 | 115 | 140 | 1.58 | 0.09 |
| Pasir Keramik liyane | 1.8 | 5.9 | 100 | 140 | 1.52 | 0.12 |
| pasir kalsinasi (pasir silika) | 2.0 | 4.8 | 62 | 120 | 1.57 | 1.09 |
Wigati: Model resin lan jumlah sing ditambahake padha, lan pasir mentah yaiku model 70/140 (sekitar AFS65), lan kondisi lapisan sing padha.
Tes reklamasi termal
| Pasir Keramik Lebur (ireng) | Cerabeads | Pasir Keramik Sintered Kaist | |
| mentahan wedhi | |
|
|
| 10 Wektu dibalekake maneh | | |
|
|
| Werna mboko sithik dadi luwih entheng, luwih peteng, putih lan kuning;partikel gedhe duwe bolongan, lan partikel bubuk cilik duwe adhesi. | Werna mboko sithik dadi luwih entheng lan kuning;ora ana owah-owahan sing katon (mung ana bolongan ing partikel gedhe). | Werna dadi kuning sawise dipanggang, lan ora ana owah-owahan sing jelas. |
Adhedhasar analisis komparatif data tes ing ndhuwur, kita nggawe kesimpulan ing ngisor iki:
①Pasir Keramik Gabungan (ireng), Cerabeads, Pasir Keramik Sintered Kaist, lan pasir keramik sinter liyane kabeh bahan refraktori aluminosilikat.Dibandhingake karo pasir calcined (pasir silika), nduweni kaluwihan saka refractoriness dhuwur, expansion termal kurang, koefisien sudut cilik, lan permeabilitas online apik.；
②Kepadhetan akeh pasir Keramik Sintered Kaist cedhak karo pasir silika, sing luwih entheng tinimbang pasir Keramik Fused lan Cerabeads.Ing bobot sing padha, jumlah wedhi Keramik Sintered Kaist sing digunakake dening pelanggan kanggo nggawe inti luwih akeh tinimbang wedhi Keramik Fused lan Cerabeads;
③Liwat perbandingan indeks wedhi sing dilapisi Resin, kita nemokake manawa pasir Keramik Sintered Kaist nduweni kinerja komprehensif sing paling apik, mung nomer loro tinimbang pasir Keramik Fused ing kinerja kekuatan, nanging wektu tahan suhu lan tekanan dhuwur luwih saka kaping pindho saka pasir Keramik Fused, kang temenan efek ing mecahaken masalah inti cilik rusak intine.
④Indeks pasir dilapisi Resin saka pasir Keramik Sintered Kaist luwih jelas tinimbang pasir sing dikalsinasi (pasir silika).Panggunaan pasir Keramik Sintered Kaist ing indeks sing padha bisa nyuda jumlah resin sing ditambahake, nyederhanakake jinis pasir sing dilapisi Resin asli, lan mbantu para pelanggan nambah lingkungan produksi lan manajemen Situs produksi;
Liwat tes reklamasi termal pasir Keramik, Cerabeads, lan wedhi Keramik Kaist, Kita nemokake manawa wedhi Keramik Fused bakal duwe pori-pori gedhe lan ikatan partikel cilik, sing bakal nambah jumlah resin nalika dilapisi maneh, nalika Cerabeads lan Kaist Keramik wedhi ora owah-owahan ketok, supaya padha luwih cocok kanggo regenerasi lan daur ulang.
Wektu kirim: Dec-31-2021